Product DetailsIR-600
Description:
IR-600 is a TiO2 material developed to reflect the near-infrared rays. It is recommended to be used in white or light color coating and plastic formulas, especially mid and high lightness colors. IR-600 can lower the temperature of the objects by offering its coating with a high TSR reflectance so to save the energy and reduce the cost. Its dense SiO2 and Al2O3 treatment gives IR-600 excellent durability.
Typical Properties:
|
TiO2 content |
≥90% |
|
Crystal form |
Rutile |
|
Inorganic treatment |
dense SiO2 and Al2O3 |
|
Organic treatment |
As required |
|
Oil absorption g/100g |
19 |
|
Specific gravity g/cm3 |
4.0 |
Note: All values are typical unless otherwise specified.
Architectural coating:
Formulation: synthetic resin emulsion, IR-600, fillers and functional auxiliaries (P.V.C.=48%).
Substrate: aluminum plate, Dry film thickness: 150μm.
|
Index |
L* |
TSR |
NIR |
|
IR-600 |
97.31 |
0.87 |
0.88 |
|
Competitor |
97.22 |
0.86 |
0.87 |
Medium lightness architectural coating:
|
Index |
L* |
TSR |
NIR |
|
IR-600 |
79.27 |
0.64 |
0.80 |
|
Competitor |
79.11 |
0.63 |
0.79 |
Acrylic acid - polyurethane coating:
Formulation: acrylic acid - polyurethane, IR-600, fillers. Substrate: aluminum plate, Dry film thickness:100 μm.
|
Index |
L* |
TSR |
NIR |
|
IR-600 |
98.75 |
0.88 |
0.87 |
|
Competitor |
98.46 |
0.87 |
0.86 |
Other information:
Packing:25kg/bag
Storage:Store closed container in cool, dry, well-ventilated area. Keep away from ignition source, heat and rain.
Handing:Avoid dust formation during handling. Provide appropriate exhaust ventilation at machinery and at places where dust can be generated. In case of insufficient ventilation, wear suitable respiratory equipment. Please see the Material Safety Data Sheets (MSDS) of this product for more safety information prior to use.
Building C19 ZNUSP, No. 99 Jingshiwu Road, 212009, Zhenjiang, Jiangsu, China
+86-511-89983592 +86-511-84492112
sales@chinatio2.com